Tel/Fax: +86-10-82034130 MP: +86-18911009322 Email:alloyo@126.com QQ:2801129509
     
 
 
     
  Super Austenitic Stock
   S31254 Stock
   N08367 Stock
   N08904 Stock
   N08926 Stock
   Super Austenitic Welding Consumable Stock
 
  Duplex Steel Stock
   S31803/S32205 Stock
   S32750 Stock
   Duplex Steel Welding Consumable Stock
 
  Ni & Ni-based Alloy Stock
   N07718 Stock
   N10276 Stock
   N06022 Stock
   N08020 Stock
   N08800/N08810 Stock
   N08825 Stock
   N06600 Stock
   N06625 Stock
   N04400 Stock
   N05500 Stock
   N02200/N02201 Stock
   Ni-based Alloy Welding Consumable Stock
 
  Ti & Ti-Alloy Stock
   GR.1 Stock
   GR.2 Stock
   GR.5 Stock
   GR.11 Stock
   Ti & Ti-Alloy Welding Consumable Stock
 

  Beijing AlloyO Technology
Add: Room 3421, No. 5 Building, Yihe Office Centre, #13 Huayuan Road, Haidian District, Beijing, China 100088
Tel/Fax: +86-10-82034130
MP: +86-18911009322
Email:alloyo@126.com
QQ: 2801129509
Home >>> News
     
 

904L super stainless coils are in stock

 
 
If you want to Know more about N08904,Please Click

904L super stainless coils and plates are in stock.
AlloyO has 120 tons stock.
The thickness is from 1.5mm to 25mm.
Welcome to communicate with AlloyO.

About 904L super stainless steel
Grade 904L stainless steel,also called as N08904,1.4539, is a non-stabilized austenitic stainless steel with low carbon content. This high alloy stainless steel is added with copper to improve its resistance to strong reducing acids, such as sulphuric acid. The steel is also resistant to stress corrosion cracking and crevice corrosion. Grade 904L is non-magnetic, and offers excellent formability, toughness and weldability.
Grade 904L contains high amounts of expensive ingredients, such as molybdenum and nickel. Today, most of the applications that employ grade 904L are replaced by low-cost duplex stainless steel 2205.

Corrosion Resistance
Grade 904L stainless steels have excellent resistance to warm seawater and chloride attack. The high resistance of grade 904L against stress corrosion cracking is due to the presence of high amounts of nickel in its composition. Moreover, the addition of copper to these grades develops resistance to sulphuric acid and other reducing agents in both aggressive and mild conditions.
The corrosion resistance of grade 904L is intermediate between super austenitic grades, with 6% molybdenum content, and standard 316L austenitic grades. Grade 904L is less resistant to nitric acid than grades 304L and 310L, which are free of molybdenum. This steel grade needs to be solution treated following cold working, to achieve maximum stress corrosion cracking resistance under critical environments.

Heat Resistance
Grade 904L stainless steels offer good oxidation resistance. However, the structural stability of this grade collapses at high temperatures, particularly above 400°C.

Heat Treatment
Grade 904L stainless steels can be solution heat-treated at 1090 to 1175°C, following by rapid cooling. Thermal treatment is suitable for hardening these grades.

Welding
Welding of grade 904L stainless steels can be performed using all conventional methods. This grade does not require pre-heat and post-weld heat treatments. The welding wire is ER385 and the welding eletrode comsumable is E385.

Fabrication
Grade 904L stainless steels are high purity steels with low sulphurs content. They can be machined using any standard methods. These grades can be readily bent to a small radius under cold conditions. Although subsequent annealing is not required in most cases, it should be carried out when the fabrication is performed under severe stress corrosion cracking conditions.

 

More about the material stock, chemical composition (Elements), material density, corrosion resistance, form (rod/bar/tube/plate/sheet/coil/welding/forging), welding (welding wire,welding electrode), strength, processing, heat treatment, standard, application and price, please call or email to alloyo@126.com.

 
 

 
              Beijing AlloyO Technology Co., Ltd.         Website Domain:www.SpecialMetalStock.com      
         Tel/Fax: +86-10-82034130 MP: +86-18911009322 Email:alloyo@126.com QQ: 2801129509  
         Keywords:Super Austenitic Stock,Duplex Steel Stock,Ni & Ni-based Alloy Stock,Ti & Ti-Alloy Stock,Welding Comsumable Stock
         Chemical composition, material density, corrosion properties,style and shape, welding, machining and Forming, heat treatment, standard, application, price