Tel/Fax: +86-10-82034130 MP: +86-18911009322 Email:alloyo@126.com QQ:2801129509
     
 
 
     
  Super Austenitic Stock
   S31254 Stock
   N08367 Stock
   N08904 Stock
   N08926 Stock
   Super Austenitic Welding Consumable Stock
 
  Duplex Steel Stock
   S31803/S32205 Stock
   S32750 Stock
   Duplex Steel Welding Consumable Stock
 
  Ni & Ni-based Alloy Stock
   N07718 Stock
   N10276 Stock
   N06022 Stock
   N08020 Stock
   N08800/N08810 Stock
   N08825 Stock
   N06600 Stock
   N06625 Stock
   N04400 Stock
   N05500 Stock
   N02200/N02201 Stock
   Ni-based Alloy Welding Consumable Stock
 
  Ti & Ti-Alloy Stock
   GR.1 Stock
   GR.2 Stock
   GR.5 Stock
   GR.11 Stock
   Ti & Ti-Alloy Welding Consumable Stock
 

  Beijing AlloyO Technology
Add: Room 3421, No. 5 Building, Yihe Office Centre, #13 Huayuan Road, Haidian District, Beijing, China 100088
Tel/Fax: +86-10-82034130
MP: +86-18911009322
Email:alloyo@126.com
QQ: 2801129509
Home >>> S32750 Super Duplex Steel Stock

 
  Duplex Steel Stock
UNS NO. Original Country Thickness Width Quantity
UNS S32750 Sweden/Japan/China 0.15~0.4mm 10~635mm 3 Tons
UNS S32750 Sweden/Japan/China 0.5~6.0mm 1219~1500mm 45 Tons
UNS S32750 Sweden/Japan/China 8.0~30mm 1500~2200mm 45 Tons
UNS S32750 Sweden/Japan/China 30~50mm 1500~2500mm 30 Tons
We have the Plate/Sheet Stock as following.
If you have the requirement,please send me the inquiry.

2507(UNS S32750) Duplex Stainless Steel 1.4410
Duplex Stainless Steel 2507 is a super duplex stainless steel with 25% chromium, 4% molybdenum, and 7% nickel designed for demanding applications which require exceptional strength and corrosion resistance, such as chemical process, petrochemical, and seawater equipment. The steel has excellent resistance to chloride stress corrosion cracking, high thermal conductivity and a low coefficient of thermal expansion. The high chromium, molybdenum, and nitrogen levels provide excellent resistance to pitting, crevice, and general corrosion.
The impact strength is also high. Alloy 2507 is not recommended for applications which require long exposures to temperatures above 570F because of the risk of a reduction in toughness.
This high molybdenum, chromium and nitrogen content results in excellent resistance to chloride pitting and crevice corrosion attack and the duplex structure provides 2507 with exceptional resistance to chloride stress corrosion cracking.

Chemical Analysis:
Typical values (Weight %)
C Cr Ni Mo N Others
0.020 25 7 4.0 .27 S=0.001

Standards:
ASTM/ASME .......... A240 - UNS S32750
EURONORM............ 1.4410 - X2 Cr Ni MoN 25.7.4
AFNOR.................... Z3 CN 25.06 Az

Corrosion Resistance:
--General Corrosion
The high chromium and molybdenum content of 2507 makes it extremely resistant to uniform corrosion by organic acids like formic and acetic acid. 2507 also provides excellent resistance to inorganic acids, especially those containing chlorides.
In dilute sulfuric acid contaminated with chloride ions, 2507 has better corrosion resistance than 904L, which is a highly alloyed austenitic steel grade specially designed to resist pure sulfuric acid.
Stainless steel of type 316L (2.5%Mo) cannot be used in hydrochloric acid due to the risk of localized and uniform corrosion. However, 2507 can be used in dilute hydrochloric acid. Pitting need not be a risk in the zone below the borderline in this figure, but crevices must be avoided.
--Stress Corrosion Cracking
The duplex structure of 2507 provides excellent resistance to chloride stress corrosion cracking (SCC). Because of its higher alloy content, 2507 is superior to 2205 in corrosion resistance and strength. 2507 is especially useful in offshore oil and gas applications and in wells with either naturally high brine levels or where brine has been injected to enhance recovery.
--Pitting Corrosion
Different testing methods can be used to establish the pitting resistance of steels in chloride-containing solutions. The data above were measured by an electrochemical technique based on ASTM G 61. The critical pitting temperatures (CPT) of several high-performance steels in a 1M sodium chloride solution were determined. The results illustrate the excellent resistance of 2507 to pitting corrosion. The normal data spread for each grade is indicated by the dark gray portion of the bar.
--Crevice Corrosion
The presence of crevices, almost unavoidable in practical constructions and operations, makes stainless steels more susceptable to corrosion in chloride enviroments. 2507 is highly resistant to crevice corrosion. The critical crevice corrosion temperatures of 2507 and several other high-performance stainless steels are shown above.

Mechanical Properties:
2507 combines high tensile and impact strength with a low coefficient of thermal expansion and high thermal conductivity. These properties are suitable for many structural and mechanical components. The low, ambient, and elevated temperature mechanical properties of 2507 sheet and plate are shown below. All of the test data shown are for samples in the annealed and quenched condition.
2507 is not recommended for applications which require long exposures to temperatures in excess of 570F because of the increased risk of a reduction in toughness. The data listed here are typical for wrought products and should not be regarded as a maximum or minimum value unless specifically stated.

Hot forming:
2507 should be hot worked between 1875F and 2250F. This should be followed by a solution anneal at 1925F minimum and a rapid air or water quench.

Cold Forming:
Most of the common stainless steel forming methods can be used for cold working 2507. The alloy has a higher yield strength and lower ductility than the austenitic steels so fabricators may find that higher forming forces, increased radius of bending, and increased allowance for springback are necessary. Deep drawing, stretch forming, and similar processes are more difficult to perform on 2507 than on an austenitic stainless steel. When forming requires more than 10% cold deformation, a solution anneal and quench are recommended.

Heat Treatment:
2507 should be solution annealed and quenched after either hot or cold forming. Solution annealing should be done at a minimum of 1925F. Annealing should be followed immediately by a rapid air or water quench. To obtain maximum corrosion resistance, heat treated products should be pickled and rinsed.

Welding:
2507 possesses good weldability and can be joined to itself or other materials by shielded metal arc welding (SMAW), gas tungsten arc welding (GTAW), plasma arc welding (PAW), flux cored wire (FCW), or submerged arc welding (SAW). 2507/P100 filler metal is suggested when welding 2507 because it will produce the appropriate duplex weld structure.
Preheating of 2507 is not necessary except to prevent condensation on cold metal. The interpass weld temperature should not exceed 300F or the weld integrity can be adversely affected. The root should be shielded with argon or 90% N2/10% H2 purging gas for maximum corrosion resistance. The latter provides better corrosion resistance.

Applications:
Oil and gas industry equipment
Offshore platforms, heat exchangers, process and service water systems
Fire-fighting systems, injection and ballast water systems
Chemical process industries, heat exchangers, vessels, and piping
Desalination plants, high pressure RO-plant and seawater piping
Mechanical and structural components, high strength, corrosion-resistant parts
Power industry FGD systems, utility and industrial scrubber systems, absorber towers, ducting, and piping

About the welding consumable materials, You can find more!
More about the material stock, chemical composition (Elements), material density, corrosion resistance, form (rod/bar/tube/plate/sheet/coil/welding/forging), welding (welding wire,welding electrode), strength, processing, heat treatment, standard, application and price, please call or email to alloyo@126.com.

 

 
 
              Beijing AlloyO Technology Co., Ltd.         Website Domain:www.SpecialMetalStock.com      
         Tel/Fax: +86-10-82034130 MP: +86-18911009322 Email:alloyo@126.com QQ: 2801129509  
         Keywords:Super Austenitic Stock,Duplex Steel Stock,Ni & Ni-based Alloy Stock,Ti & Ti-Alloy Stock, welding,Welding Comsumable Stock, welding
         Chemical composition, material density, corrosion properties,style and shape, machining and Forming, heat treatment, standard, application, price